The Influence of Hemp Fibers (Cannabis sativa L.) on the Mechanical Properties of Fiber–Gypsum Boards Reinforcing the Gypsum Matrix

The modern construction industry is looking for new ecological materials (available, cheap, recyclable) that can successfully replace materials that are not environmentally friendly. Fibers of natural origin are materials that can improve the properties of gypsum composites. This is an important issue because synthetic fibers (hardly biodegradable—glass or polypropylene fibers) are commonly used to reinforce gypsum boards. Increasing the state of knowledge regarding the possibility of replacing synthetic fibers with natural fibers is another step towards creating more environmentally friendly building materials and determining their characteristics. This paper investigates the possibility of manufacturing fiber–gypsum composites based on natural gypsum (building gypsum) and hemp (Cannabis sativa L.) fibers grown in Poland. The effect of introducing hemp fibers of different lengths and with varying proportions of mass (mass of gypsum to mass of fibers) into the gypsum matrix was investigated. The experimental data obtained indicate that adding hemp fibers to the gypsum matrix increases the static bending strength of the composites manufactured. The highest mechanical strength, at 4.19 N/mm2, was observed in fiber–gypsum composites with 4% hemp fiber content at 50 mm in length. A similar trend of increased strength was observed in longitudinal tension. Again, the composite variant with 4% fiber content within the gypsum matrix had the highest mechanical strength. Manufacturing fibers–gypsum composites with more than 4% hemp fiber content negatively affected the composites’ strength. Mixing long (50 mm) hemp fibers with the gypsum matrix is technologically problematic, but tests have shown a positive effect on the mechanical properties of the refined composites. The article indicates the length and quantity limitations of hemp fibers on the basis of which fiber–gypsum composites were produced.